Abstract
Basic fibroblast growth factor (bFGF)-encapsulated poly(ε-caprolactone) (PCL) nano/microfibrous scaffolds were fabricated to improve cell viability and tissue regeneration. bFGF-encapsulated PCL nanofibers and microfibers were fabricated by emulsion electrospinning and melt-electrospinning, respectively. Electrospinnability of emulsions was improved with the addition of Pluronic F-127 because emulsions containing Pluronic F-127 had a high affinity for both water and oil phases. The core-shell structure of protein-encapsulated nanofiber component was observed by a confocal laser scanning microscope (CLSM). From results of CLSM observation, it was found that the protein-loaded particle's size and their loading efficiency inside nanofibers were influenced by the addition of emulsifiers and the concentration thereof. Also, the 'Protein/SA' group contained a viscoelastic water phase with smaller particles in the core of nanofibers than the 'Protein only' group does. From protein release behavior, it was apparent that protein-encapsulated nanofibers prepared by emulsion electrospinning were stable in water environments and were only released in Na ion-containing medium such as bodily fluids. In vitro cell proliferation, the optical density of the 'Protein/SA' group with bFGF at 490 nm was slight higher than that of the 'None' and 'Protein only' group during the period of cell culture. In vivo bone regeneration, bFGF-encapsulated nano/microfibrous composite scaffold is the only group that new bone was formed to the center of the defect. Consequently, the potential use of bFGF-encapsulated nano/microfibrous composite scaffolds in bone regeneration fields was suggested.
Original language | English |
---|---|
Article number | 18044 |
Pages (from-to) | 8-16 |
Number of pages | 9 |
Journal | Polymer |
Volume | 76 |
DOIs | |
State | Published - 12 Oct 2015 |
Keywords
- Bone regeneration
- Nano/microfibrous composite scaffolds
- Poly(ε-caprolactone) (PCL)