Formation of low-resistivity nickel silicide with high temperature stability from atomic-layer-deposited nickel thin film

Kwan Woo Do, Chung Mo Yang, Ik Su Kang, Kyung Min Kim, Kyoung Hum Back, Hyun Ick Cho, Heon Bok Lee, Sung Ho Kong, Sung Ho Hahm, Dae Hyuk Kwon, Jong Hyun Lee, Jung Hee Lee

Research output: Contribution to journalArticlepeer-review

47 Scopus citations

Abstract

Nickel suicide (NiSi) was formed by annealing a uniform low-resistivity nickel (Ni) film deposited by atomic layer deposition (ALD). A Ni film as-deposited at 220°C exhibited the lowest sheet resistance of 18Ω/sq. comparable to that of the film obtained by physical vapor deposition, even though it contained a significant amount of carbon from the metalorganic precursor. It is believed that the carbon is uniformly distributed in the film by partly forming a weak Ni3C phase which eliminates other crystalline defects in the film and hence lowers the resistance of the film. However, the carbon was not observed at the Ni/Si interface and in the silicon bulk except at the film surface after the annealing to form silicide. The existence of carbon at the surface of the film causes the film to maintain a low-resistivity NiSi phase up to 800°C, without the carbon at the surface, the phase of film is changed to the high-resistivity nickel disilicide (NiSi2) at such a high temperature. The deposition of Ni by ALD and the formation of low-resistivity NiSi with an increased temperature stability can be useful in fabricating advanced devices, such as nanometer scale complementally metal-oxide silicons (CMOSs) or three-dimensional (3-D) MOS devices like Fin-type field-effect transistors (Fin-FETs).

Original languageEnglish
Pages (from-to)2975-2979
Number of pages5
JournalJapanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
Volume45
Issue number4 B
DOIs
StatePublished - 25 Apr 2006

Keywords

  • Atomic layer deposition
  • Nickel disilicide
  • Nickel suicide
  • Sheet resistance

Fingerprint

Dive into the research topics of 'Formation of low-resistivity nickel silicide with high temperature stability from atomic-layer-deposited nickel thin film'. Together they form a unique fingerprint.

Cite this