Nanodiamond islands confined between two graphene sheets as perspective 2D quantum materials

Based on direct space DFT PBE0/6-31G* electronic structure calculations, the structure and properties of nanodiamond islands confined between two finite graphene fragments (NDI-c2G) was proposed and theoretically explored. DFT simulations revealed that fusion of planar aromatic molecules with two parent graphene fragments may form either cubic or hexagonal allotropes of NDI-c2Gs lattices accompanied with formation of local corrugated sp³ sites with substituted dangling bonds embedded into graphene sublattices. It was shown that at the DFT level of theory, low distortion energies of NDI-c2Gs lattices are comparable or smaller than the energy of van-der-Waals interactions, which allows the NDI-c2G lattices to be stabilized by a support and finally synthesized. The Nuclear Independent Chemical Shift calculations, shows that in the vicinity of NDI regions, graphene lattices are estimated to be either low-, or anti-aromatic. Furthermore, the formation of NDI-c2Gs leads to localization of HOMO and LUMO states at different sites of the NDI-c2Gs lattices. The NDI-c2G regions with confined frontier orbitals can be considered as arrays of quantum dots isolated from each other by NDI scattering centres of 3.82 Å dimension. The results demonstrates that NDI-c2G should be considered as strongly-correlated entangled hybrid quantum dots which may form extended quantum ensembles with great potential for advanced quantum applications.