Organic-inorganic hybrid compounds containing polyhedral oligomeric silsesquioxane for conservation of stone heritage

Alkoxysilane solutions based on tetraethoxysilane (TEOS) have been widely used for the consolidation of decaying heritage stone surfaces. TEOS-based products polymerize within the porous structure of the decaying stone, significantly increasing the cohesion of the grains of stone components. However, they suffer from practical drawbacks, such as crack formation of the gel during the drying phase due to the developing capillary force and dense gel fractures left inside of the stone. In this study, a TEOS-based stone consolidant containing functional (3-glycidoxypropyl)trimethoxysilane (GPTMS) and polyhedral oligomeric silsesquioxane (POSS) has been prepared in order to reduce gel crack formation during the drying phase. The addition of nanometer-sized POSS and/or GPTMS having a flexible segment reduces the capillary force developed during solvent evaporation. The properties of the TEOS/GPTMS/POSS composite solutions were compared with those of commercial products (Wacker OH and Unil sandsteinfestiger OH 1:1). The gelation time was similar to that of commercial consolidants, and the TEOS/GPTMS/POSS solution was stable over a period of up to 6 months. The addition of POSS and GPTMS provided a crack-free gel, while the gel from the commercial consolidants exhibited cracks after drying. The surface hydrophobicity of the treated decayed granite increased with the addition of POSS and GPTMS, and it was higher than that of the commercial product, implying the possibility of POSS and GPTMS as barriers to the penetration of water. This result implies that the TEOS/GPTMS/POSS solution showed a high suitability for the consolidation of granite heritage.