Sintering and dielectric properties of Li2O - B 2O3 - Al2O3 - SiO2 glass-added (Ca 0.7 Sr 0.3 O)1.03(Ti 0.1 Zr 0.9) O 2 for copper electrode

Hyunho Shin; Sang Wook Lee; Hyun Suk Jung

doi:10.1111/j.1744-7402.2012.02782.x

Sintering and dielectric properties of Li₂O - B ₂O₃ - Al₂O₃ - SiO₂ glass-added (Ca _0.7 Sr _0.3 O)_1.03(Ti _0.1 Zr _0.9) O ₂ for copper electrode

Hyunho Shin, Sang Wook Lee, Hyun Suk Jung

Research output: Contribution to journal › Article › peer-review

10 Scopus citations

Abstract

When 1.5 wt% of Li₂O-B₂O₃-SiO₂ and 1.5 wt% of Li₂O-B₂O₃-Al₂O ₃ glass-added (Ca_0.7Sr_0.3O) _1.03(Ti_0.1Zr_0.9)O₂ batch was ball milled for 10~30 h followed by sintering at 950°C in flowing N ₂-10%H₂ atmosphere, an apparent density of approximately 4.5 g/cm³, a dielectric constant of approximately 26, and a quality factor of roughly about 3300 GHz were demonstrated. A prolonged ball mill time thereafter significantly decreased both of the dielectric properties because of the enhanced reduction of the specimens during sintering. The apparent evidence of a material reaction between the dielectric material and the copper electrode was not observed.

Original language	English
Pages (from-to)	716-722
Number of pages	7
Journal	International Journal of Applied Ceramic Technology
Volume	10
Issue number	4
DOIs	https://doi.org/10.1111/j.1744-7402.2012.02782.x
State	Published - Jul 2013

Access to Document

10.1111/j.1744-7402.2012.02782.x

Cite this

@article{9dbce74adc86461eb8756a4cd45bcd80,

title = "Sintering and dielectric properties of Li2O - B 2O3 - Al2O3 - SiO2 glass-added (Ca 0.7 Sr 0.3 O)1.03(Ti 0.1 Zr 0.9) O 2 for copper electrode",

abstract = "When 1.5 wt\% of Li2O-B2O3-SiO2 and 1.5 wt\% of Li2O-B2O3-Al2O 3 glass-added (Ca0.7Sr0.3O) 1.03(Ti0.1Zr0.9)O2 batch was ball milled for 10\textasciitilde{}30 h followed by sintering at 950°C in flowing N 2-10\%H2 atmosphere, an apparent density of approximately 4.5 g/cm3, a dielectric constant of approximately 26, and a quality factor of roughly about 3300 GHz were demonstrated. A prolonged ball mill time thereafter significantly decreased both of the dielectric properties because of the enhanced reduction of the specimens during sintering. The apparent evidence of a material reaction between the dielectric material and the copper electrode was not observed.",

author = "Hyunho Shin and Lee, \{Sang Wook\} and Jung, \{Hyun Suk\}",

year = "2013",

month = jul,

doi = "10.1111/j.1744-7402.2012.02782.x",

language = "English",

volume = "10",

pages = "716--722",

journal = "International Journal of Applied Ceramic Technology",

issn = "1546-542X",

publisher = "Wiley-Blackwell",

number = "4",

}

TY - JOUR

T1 - Sintering and dielectric properties of Li2O - B 2O3 - Al2O3 - SiO2 glass-added (Ca 0.7 Sr 0.3 O)1.03(Ti 0.1 Zr 0.9) O 2 for copper electrode

AU - Shin, Hyunho

AU - Lee, Sang Wook

AU - Jung, Hyun Suk

PY - 2013/7

Y1 - 2013/7

N2 - When 1.5 wt% of Li2O-B2O3-SiO2 and 1.5 wt% of Li2O-B2O3-Al2O 3 glass-added (Ca0.7Sr0.3O) 1.03(Ti0.1Zr0.9)O2 batch was ball milled for 10~30 h followed by sintering at 950°C in flowing N 2-10%H2 atmosphere, an apparent density of approximately 4.5 g/cm3, a dielectric constant of approximately 26, and a quality factor of roughly about 3300 GHz were demonstrated. A prolonged ball mill time thereafter significantly decreased both of the dielectric properties because of the enhanced reduction of the specimens during sintering. The apparent evidence of a material reaction between the dielectric material and the copper electrode was not observed.

AB - When 1.5 wt% of Li2O-B2O3-SiO2 and 1.5 wt% of Li2O-B2O3-Al2O 3 glass-added (Ca0.7Sr0.3O) 1.03(Ti0.1Zr0.9)O2 batch was ball milled for 10~30 h followed by sintering at 950°C in flowing N 2-10%H2 atmosphere, an apparent density of approximately 4.5 g/cm3, a dielectric constant of approximately 26, and a quality factor of roughly about 3300 GHz were demonstrated. A prolonged ball mill time thereafter significantly decreased both of the dielectric properties because of the enhanced reduction of the specimens during sintering. The apparent evidence of a material reaction between the dielectric material and the copper electrode was not observed.

UR - https://www.scopus.com/pages/publications/84879781106

U2 - 10.1111/j.1744-7402.2012.02782.x

DO - 10.1111/j.1744-7402.2012.02782.x

M3 - Article

AN - SCOPUS:84879781106

SN - 1546-542X

VL - 10

SP - 716

EP - 722

JO - International Journal of Applied Ceramic Technology

JF - International Journal of Applied Ceramic Technology

IS - 4

ER -

Sintering and dielectric properties of Li₂O - B ₂O₃ - Al₂O₃ - SiO₂ glass-added (Ca _0.7 Sr _0.3 O)_1.03(Ti _0.1 Zr _0.9) O ₂ for copper electrode

Abstract

Access to Document

Other files and links

Fingerprint

Cite this