Trap level analysis of Ce 3+ and Sm 3+ in Li 6 Y(BO 3 ) 3

D. Joseph Daniel, H. J. Kim, Sunghwan Kim, S. Kothan, J. Kaewkhao

Research output: Contribution to journalArticlepeer-review

5 Scopus citations

Abstract

The polycrystalline compounds of Li 6 Y(BO 3 ) 3 : Ce 3+ and Sm 3+ co-doped polycrystalline samples were prepared by using standard solid state reaction method. The energy levels of the doped lanthanide ions (Ce 3+ and Sm 3+ ) in the borate host materials were investigated by Thermoluminescence (TL) glow peak analysis. The co-doped samples, exhibits the TL peak at higher temperature region around 511 K whereas the Ce 3+ individually doped sample has peak around 433 K. The X-ray excited emission spectra were carried out for all the prepared samples and found the characteristic emission bands. The trap depths (E) were calculated by using several standard methods, namely peak shape method or chen's (PS), variable heating rate (VHR), initial rise (IR) and computerized glow curve deconvolution (CGCD). The mean activation energy of the co-doped samples found to be 1.21 (0.07±) eV and the frequency factor around 1.38 × 10 11 Sec −1 . The calculated trap depths and the predicted energy level values were compared and found in good agreement. This primarily results suggest that the energy level scheme can help in the development of new TL materials suitable in dosimetry.

Original languageEnglish
Pages (from-to)11893-11898
Number of pages6
JournalCeramics International
Volume45
Issue number9
DOIs
StatePublished - 15 Jun 2019

Keywords

  • A. polycrystalline
  • B. thermoluminescence
  • C. energy level
  • D. activation energy

Fingerprint

Dive into the research topics of 'Trap level analysis of Ce 3+ and Sm 3+ in Li 6 Y(BO 3 ) 3'. Together they form a unique fingerprint.

Cite this